产品名称MIM-TC4化学成分wt.%TiOCHNFe余量≤0.18≤0.020.0120.020.25AlV5.5-6.53.5-4.5物理性能粒度范围/μm振实密度D10D50D90g/cm35.0-7.010.0-13.516.0-22.0≥2.85烧结后化学成分wt.%TiOCHNFe余量≤0.35≤0.10.0150.040.3AlV5.5-6.753.5-4.5烧结件特性密度屈服强度极

产品名称	MS1
chemical composition wt.%	O	Fe	C	Mn	Si	Cr
	≤0.03	Bal.	≤0.03	≤0.1	≤0.1	≤0.5
	S	P	Mo	Ni	Co	Ti
	≤0.01	≤0.01	4.8	18	9.0	0.7
	Al
	0.1
physical properties	size distribution μm	hall flow s/50g	apparent density g/cm³	tap density g/cm³	oxygen content ppm	sphericity %
physical properties	15-53	≤16	≥4.2	≥4.8	≤300	≥85
Performance after printing	Rockwell hardness HRC	tensile strength MPa	yield strength MPa	elongation %	Polishing property SPI:B1｜Ra：～0.01μm｜gaps above 20μm < 20 /cm²
Performance after printing	54-57	2000	1980	5